dc.identifier.citationMurathan, A., Asan, A., Abdulkarem, T. (2013). Çevresel Atıkların Yapı Malzemesinde Değerlendirilmesi. Gazi Üniversitesi Mühendislik-Mimarlık Fakültesi Dergisi, 28(2).en_US
dc.identifier.issn1300-1884
dc.identifier.urihttps://hdl.handle.net/11491/2997
dc.descriptionresearchen_US
dc.description.abstractBu çalışmada, Türkiye’de yeralan bazı çevresel atıklar tuğla kilinde kullanılarak kompozit malzeme üretilmiştir. Kompozit malzeme üretiminde ana hammadde Reşadiye kili; dolgu malzemeleri ise Kütahya- Emet Bor İşletmesi bor atığı, Seyitömer Termik Santral uçucu külü ve Ankara-Tatlar Atıksu Arıtma Tesisi arıtma çamurudur. Değişik kaynaklardan elde edilen numuneler önce öğütülmüş daha sonra değişik oranlarda iyice karıştırılmış, nemlendirilmiş ve kalıplara dökülmüştür. Deneylerde kütle temel alınmak üzere kompozitlerde bor atığı % 2,5-20; uçucu kül % 2,5-10; arıtma çamuru % 0-10 ve tuğla kili % 75-85 oranında kullanılmıştır. 50x50x50 mm ebadındaki küp numuneler sırasıyla oda sıcaklığında 24 saat, daha sonra 105±1 °C’de 12 saat kurutulmuştur. Birim hacim ağırlığı, kuruma küçülmesi, su emme, basınç dayanımı ve kütle kaybı deneyleri sonunda, TS EN 771-1 standardı olan tuğla fiziksel parametrelerine kısmen yaklaşıldığı tespit edilirken aynı zamanda enerji tasarruflu ve çevre dostu kompozit malzeme üretilmiştir.en_US
dc.description.abstractIn this study, it was produced composite material by using environmental waste sources of Turkey in brick clay. It was selected Reşadiye Clay as main material and boron waste of Kütahya-Emet Boron Works, fly ash of Seyitömer Power Plant and wastewater treatment sludge of Ankara- Tatlar Wastewater Treatment Plant as filling materials. Obtained samples from various resources were firstly grinded, then well mixed in different ratios, moistened and poured into the molds. In the experiments mass percent of boron waste, fly ash and treatment sludge were changed in composites respectively between (2.5-20%), (2.5-10%) and (0-10%) and brick clay was used between 75-85%. Shaped samples which have 50x50x50 mm dimension were dried at room temperature for 24 hours and after that at 105±1 °C for 12 hours respectively. Specific bulk density, drying shrinkage, water absorption, compressive strength and loss of mass tests were carried out. At the end of the tests, it has been conclused approach to the TS EN 771-1 brick standard physical parameters partly also, it has been produced energy conservative and environmentally friendly composite material.en_US
dc.language.isoturen_US
dc.rightsinfo:eu-repo/semantics/openAccessen_US
dc.subjectKompozit Malzemeen_US
dc.subjectTuğla Kilien_US
dc.subjectBor Atığıen_US
dc.subjectUçucu Külen_US
dc.subjectArıtma Çamuruen_US
dc.subjectBasınç Dayanımıen_US
dc.subjectBirim Hacim Ağırlığıen_US
dc.titleÇevresel atıkların yapı malzemesinde değerlendirilmesien_US
dc.title.alternativeEvaluation of environmental wastes in building materialen_US
dc.typearticleen_US
dc.relation.journalGazi Üniversitesi Mühendislik Mimarlık Fakültesi Dergisien_US
dc.departmentHitit Üniversitesi, Mühendislik Fakültesi, Kimya Mühendisliği Bölümüen_US
dc.identifier.volume28en_US
dc.identifier.issue2en_US
dc.identifier.startpage409en_US
dc.identifier.endpage416en_US
dc.relation.publicationcategoryMakale - Ulusal Hakemli Dergi - Kurum Öğretim Elemanıen_US


Bu öğenin dosyaları:

Thumbnail

Bu öğe aşağıdaki koleksiyon(lar)da görünmektedir.

Basit öğe kaydını göster