Cell-Based Experimental Analysis of a Proton Exchange Membrane Fuel Cell (PEMFC)

Abstract

This study is focused on cell-based experimental analysis of Proton Exchange Membrane Fuel Cell (PEMFC) with sodium borohydride (NaBH4). The change in cell-based voltage values of 10-cell PEM fuel cell at two different temperatures was evaluated by keeping at constant load NaBH4, pure water and citric acid (C6H8O7) which is used as a catalyzer. 3 g NaBH4, H2O/NaBH4: 2 mol/mol (x=0), and C6H8O7 catalyzer/NaBH4: 0.1 g/g and 250 cm3 of reactor volume production were realized. When the water temperature was raised to 60 ºC from 40 ºC, total voltage value increased by 6.1%. While, in the experiment of 40 ºC, the interchange in voltage values were between 0.53 V and 0.78 V, the mean values in the experiment of 60 ºC were between 0.61 V and 0.79 V.

Bu çalışma, sodyum borhidrür (NaBH4) kullanılan bir proton değiştirme membranı (PEM) yakıt pilinin hücre bazlı deneysel analizi üzerine odaklanmıştır. NaBH4, saf su ve katalizör olarak kullanılan sitrik asit (C6H8O7) sabit yükte tutularak iki farklı sıcaklıkta 10 hücreli PEM yakıt pilinin hücre bazlı gerilim değerlerindeki değişim değerlendirilmiştir. 3 g NaBH4, H2O/NaBH4: 2 mol/mol (x=0) ve C6H8O7 katalizörü/NaBH4: 0.1 g/g ile 250 cm3 reaktör hacminde hidrojen üretimi gerçekleştirilmiştir. Su sıcaklığı 40 ºC’den 60 ºC’ye çıkarıldığında toplam gerilim değeri % 6.1 oranında artmıştır. 40 °C deneyinde ortalama gerilim değerleri 0.53 V ila 0.78 V arasında değişirken 60 °C deneyinde ise ortalama değerler 0.61 V ila 0.79 V arasında değişmiştir.