dc.identifier.citationBağcı, C., Kutyla, G. P., Kriven, W. M. (2017). Fully reacted high strength geopolymer made with diatomite as a fumed silica alternative. Ceramics International, 43(17), 14784-14790.en_US
dc.identifier.issn0272-8842
dc.identifier.urihttps://doi.org/10.1016/j.ceramint.2017.07.222
dc.identifier.urihttps://hdl.handle.net/11491/820
dc.description.abstractGeopolymers are formed by mixing of aluminosilicate sources with alkaline meta-silicate solution at room temperature. In the current study, diatomite of Turkish origin was fully utilized as a fumed silica alternative for the preparation of geopolymer, having a typical formula of K2O•Al2O3•4SiO2•11H2O. From XRD of this sample, a broad peak centered at 28° 2? indicated the well-known formation of amorphous geopolymer, as well as a fully reacted microstructure of geopolymer as seen by scanning electron microscopy. Additionally, geopolymer having the same formula was made by using fumed silica, in order to compare with geopolymers prepared from diatomite. The Weibull modulus was calculated from four-point bending and compressive strength testing of both geopolymer composites. The use of diatomite as a fumed silica substitute in geopolymer production resulted in a very close flexure strength 9.2 (± 4.2 MPa) when compared to geopolymer made from fumed silica 10.2 (± 3.3 MPa). There was a significantly higher compressive strength 71 (± 13.9 MPa) and Weibull modulus (5.4), than comparable properties of geopolymer made from fumed silica, which had a compressive strength 54 (± 25.8 MPa) and Weibull modulus of 2.0. The discrepancy was attributed to some self-reinforcement of the geopolymer matrix due to unreacted diatomite. © 2017 Elsevier Ltd and Techna Group S.r.l.en_US
dc.language.isoeng
dc.publisherElsevier Ltden_US
dc.relation.isversionof10.1016/j.ceramint.2017.07.222en_US
dc.rightsinfo:eu-repo/semantics/closedAccessen_US
dc.subjectDiatomiteen_US
dc.subjectFumed Silicaen_US
dc.subjectGeopolymeren_US
dc.titleFully reacted high strength geopolymer made with diatomite as a fumed silica alternativeen_US
dc.typearticleen_US
dc.relation.journalCeramics Internationalen_US
dc.departmentHitit Üniversitesi, Mühendislik Fakültesi, Metalurji ve Malzeme Mühendisliği Bölümüen_US
dc.authorid0000-0001-9931-0778en_US
dc.identifier.volume43en_US
dc.identifier.issue17en_US
dc.identifier.startpage14784en_US
dc.identifier.endpage14790en_US
dc.relation.publicationcategoryMakale - Uluslararası Hakemli Dergi - Kurum Öğretim Elemanıen_US


Bu öğenin dosyaları:

DosyalarBoyutBiçimGöster

Bu öğe ile ilişkili dosya yok.

Bu öğe aşağıdaki koleksiyon(lar)da görünmektedir.

Basit öğe kaydını göster